氮化硅陶瓷韧化的研究与进展

马光华　汪永清

(景德镇陶瓷学院)

摘　要

本文阐述了氮化硅陶瓷的增韧补强的研究与进展,对氮化硅的几种常见增韧补强的途径如弥散增韧、纤维增韧、相变增韧、自增韧、层状复合增韧作了评述,指出了目前进行氮化硅陶瓷的增韧的途径与方向。关键词:氮化硅,弥散增韧,纤维增韧,相变增韧,自增韧,层状复合增韧中图法分类号:TQ174.25　　　文献标识码:A

STUDYONANDPROGRESSINNITRIDEWangYongqin

JingdezhenCeramicInstitute)

Abstract

Inthepaper,thestudyonandtheprogressintoughenedandreinforcedsiliconnitrideceramicsareexpounded,andtheconventionalavenuestotoughsiliconnitrideceramicsarecommentedsuchasdispersiontoughing,fiberreinforcing,phasetransformationtoughing,selftoughingandlamellarcompoundtoughing.Finallytheavenuesanddirectionarepointedouttotoughensiliconnitrideceramics.

Keywords　siliconnitrideceramicsdispersiontougherning,fiberreinforcing,phasetransformationtoughening,selftoughening,

lamellarcompoundtougherning

但是,因氮化硅陶瓷的脆性缺陷未得到彻底的改

1　前　言

氮化硅陶瓷是典型的高温高强结构陶瓷,具有良好的室温及高温机械性能,强度高,耐磨蚀,抗热震能力强,抗化学腐蚀,低导热系数,比重相对较小,是结构陶瓷中研究最为广泛深入的材料,亦是陶瓷发动机及其它高温结构件、切削工具、耐磨件等的主要候选材料。近几年来仍是人们争相研究的热点。

收稿日期:2001-04-10

作者简介:马光华,景德镇陶瓷学院材料工程系教授,333001

善,故而大大限制了它的实际应用。如何提高氮化硅韧性仍是Si3N4陶瓷研究的焦点。目前从事氮化硅陶瓷研究的学者为了提高氮化硅陶瓷的韧性,主要从两大方面着手进行研究。一是通过进行“显微结构设计”来提高氮化硅陶瓷的韧性。即降低气孔的含量,控制杂质的含量,提高氮化硅陶瓷的密度、纯度;对氮硅陶瓷的晶型、晶粒尺寸、发育完整程度进行控制;对晶界的大小、材质进行调控;对玻璃相的数量、性质、分布状